Martensitic Stainless Steels Low-temperature Nitriding: Dependence of Substrate Composition

W1023185386 · 수집 2026-10-04 18:06:55

T10377 Metal and Thin Film Mechanics

CoT 라벨링

라벨링 전

PDF 파일

저장된 PDF 없음

기본 정보

DOI 제목 발행년도 저널 URL 페이지 열기 PDF URL PDF 열기 발행기관 피인용수 라이선스

추가 정보 초록

Low-temperature plasma assisted nitriding is a very promising technique to improve surface mechanical properties of stainless steels, keeping unaltered or even improving their surface corrosion resistance. During treatment, nitrogen diffuses into the steel surface, increasing its hardness and wear resistance. In the present work the nitriding process of different martensitic stainless steels was studied. As-quenched AISI 410, 410NiMo, 416 and 420 stainless steel samples were plasma nitrided at 300, 350, 400, 450, and 500°C, for 4 h, at 3 Torr, in a gas mixture of 70% N2 + 20% H2 + 10% Ar, and flow rate of 3.33×10–6 Nm3s−1. The study of the nitrogen-rich layer thickness indicates two different activation energies, one for low (<400°C) and another one for high temperature ( ≥400°C), except for the AISI 410NiMo. The surface hardness increases with temperature for all steels between 300 and 450°C. For 500°C, except for the AISI 410NiMo, the surface hardness decreases if compared to that obtained at 450°C. This hardness decrease is related to chromium nitride precipitation, also associated to the treated surface sensitization. Finally, the CrN precipitation in treated surfaces is dependent on the steel composition, with the AISI 410NiMo steel presenting the lower average chromium nitride precipitation rate.

본문 활용가능성

이력 0건

아직 편집 이력이 없습니다. 저장할 때마다 이전 내용이 여기에 백업됩니다.